Advantage
1. Less overflowing : lower Milt index 5-6;
2. Best optical performance and safety performance : 85-95% cross-linking at 130- 150°C laminating.
3. Superior water-proof: open edge application
4. Best anti-aging and durability in outdoor application.
5. Crystalline particle control make EVA film more transparency and cleanliness.
Specification
1. The best mechanical performance:
|
Cross-linking
|
Extracted in Xylene Solution
|
>95%(after 150℃ 25mins laminating)
|
|
Tensile strength
|
>21MPA
|
|
Adhesion with glass
|
>95N/cm
|
|
Water absorption
|
<0.1%
|
2.Superior optical performance:
|
Light transmittance
|
>91%
|
|
Haze
|
<0.2%
|
|
UV filtering
|
>99%(390nm wavelength)
|
|
Lighting transmittance decrease
|
<0.5%(2000hrs UV radiation)
|
|
Yellow index(YI)
|
<3(2000hrs UV radiation)
|
3.Best durability an stability in outdoor climate application:Heat and humidity resistance,Radiation resistance,ball impact peeling test and shot bag impact have been tested for laminated glass with norminal thickness according to GB15763.3-2009 safety glazing materials in building-Part3:Laminated glass
|
Boilding test(2hrs into 100℃ water)
|
5mm glass+0.80mm EVA+5mm glass
|
Good
|
|
Heat and Humidity resistance test
|
85℃ 85%RH,1000hrs
|
Good
|
|
Anti-aging test
|
50℃ 65%RH,UV radiation 2000hrs
|
Good
|
|
Heat and cold shock test
|
-40℃ 30mins/80℃ 30mins,50 circles
|
Good
|
|
impact resistance against shot-bag
|
GB-15763.3-2009
|
Qualified
|
|
Ball impact peeling resistance
|
GB-15763.3-2009
|
Qualified
|
Instructions
1. Prepare and cut the EVA film into right size according to the following structure:
glass+EVA film + glass
2. Put the overlapped glass into silicon bag and seal silicon bag well.
3. Activate vacuum pump for 5-8min till vacuum value reach -0.095Mpa to double checking the vacuum is good.
4 Set up the laminating temp. and time and start heating.The following data based on 5mm glass +0.40mm EVA +5mm glass.
| |
Heating speed
|
Temp. and holding time
|
Vaccum Value
|
|
First section
|
2℃/min
|
60℃
|
25mins
|
-0.095MPA
|
|
Second section
|
2℃/min
|
80℃
|
30mins
|
-0.095MPA
|
|
Third section
|
2℃/min
|
135℃
|
45mins
|
-0.04MPA
|
Remark: The above curves only for reference, the user should do some adjusts according to the process surroudings(temperature and humidity), glass area, glass thicknes,glass type and the machine itself.